1. Caracterização microestrutural da decomposição de carbonetos eutéticos M2C em ferro fundido multicomponente do tipo Fe-2C-5V-5Cr-5Mo-5W tratados isotermicamente à 950ºC e 1.050ºC. / Microstructural characterization of M2C eutectic carbides decomposition in multicomponent cast iron of type Fe-2C-5V-5Cr-5Mo-5W isothermically heat treated at 950°C e 1.050°C.
Multicomponent White Cast Iron are high temperature wear resistant ferrous alloys, presenting eutectic MC and M2C carbides in their as cast structure. In the present work the decomposition microstructures of the metastable M2C carbide after heat treatments was characterized in a model multicomponent white cast iron with composition (in weight): 2 wt% C and 5
Publicado em: 2010
-
2. Obtenção de compósitos de matriz metálica através da adição de TiCN e Wc na base HSS tipo M2 via metalurgica do pó
Os aços rápidos constituem desde o final do século XIX uma importante classe de materiais de elevado desempenho para utilização em ferramentas de usinagem e como componentes estruturais. Estes materiais constituem-se basicamente de uma matriz martensítica contendo carbonetos primários de 1 10 m em diâmetro, formados durante a solidificação do aço
Publicado em: 2003
-
3. Fracture toughness of as-cast high speed steel M2, modified and heat treated. / Estudo da tenacidade à fratura do aço rápido M2 fundido, modificado e tratado termicamente.
Neste trabalho foi medida a tenacidade à fratura de quatro ligas fundidas com composição química base do aço AISI M2 uma de composição química convencional (liga I), e as demais modificadas por adições de nitrogênio (liga II), cério (liga III) e antimônio (liga IV) submetidas a tratamentos térmicos visando a decomposição do carboneto M2