Aluminium Copper Alloys
Mostrando 1-6 de 6 artigos, teses e dissertações.
-
1. Tensile and fatigue properties, machinability and machined surface roughness of Al-Si-Cu alloys
ABSTRACT In this paper, the aim was to determine if ASC91 (9 % Al, 1 % Cu) could be replaced with ASC73 (7 % Al, 3 % Cu) aluminium alloy, with presumably improved machinability due to lower silicon content (9 to 7 %) and retained mechanical properties due to a higher copper content (1 to 3 %). The test samples were excised from cylinder heads produced by the
Matéria (Rio J.). Publicado em: 16/09/2019
-
2. Damping of Fe-Al Alloy Electrodeposited in an Ionic Liquid
Iron-Aluminium alloys were produced by the electro-deposition of iron-aluminium on a copper substrate. The electro-deposition process was done in the ionic liquid 1-butyl-1-methylpyrrolidinium trifluoromethylsulfonate, [Py1,4]TfO. A solution of (0.2 M FeCl2 + 2.75 M AlCl3)/ [Py1,4] TfO was used at a temperature of T=363 K because this mixture is solid at roo
Mat. Res.. Publicado em: 11/10/2018
-
3. Avaliação da tixoconformabilidade das ligas AA 2011 e AA 2014 / Avaliation of the thixoconformability of AA 2011 and AA 2014 alloys
A tixoconformação é uma técnica de processamento de materiais no estado semi-sólido que permite a produção de peças com geometrias near net shape com melhores propriedades mecânicas e com razoável redução no custo final de produção, se comparados aos métodos de fundição e conformação plástica tradicionais. Dentro das várias possibilidade
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 01/07/2010
-
4. Analysis of the solidification uner radial heat flow / Analise da solidificação sob fluxo de calor radial cilindrico
Apesar da importância tecnológica da solidificação de ligas metálicas sob fluxo de calor radial, relativamente poucos estudos estão sendo feitos nessa área. Neste trabalho, a solidificação da liga Al 4,5%Cu em molde de aço radial cilíndrico é analisada e comparada com a solidificação direcional em molde resfriado.Inicialmente a variação de te
Publicado em: 2007
-
5. Corrosion performance of Al-Si-Cu hypereutectic alloys in a synthetic condensed automotive solution
In this investigation the corrosion resistance of four Al-Si hypereutectic alloys in a solution typical of condensate from automotive fuel combustion products, and referred to here as synthetic condensed automotive solution, has been studied. Three commercial alloys that are used for cylinder liners, and a laboratory made alloy, were studied by electrochemic
Materials Research. Publicado em: 2005-06
-
6. Caracterização da microestrutura dendritica na solidificação vertical descendente de ligas AL-CU / Characterization of dendritic array during downward transient directionally solidified AL-CU alloys
The dendritic spacings are important microstructural parameters, involved in solidification processes. They can affect not only microsegregation profiles but also the formation of secondary phases within interdendritic regions, which influences mechanical properties of cast structures. A small number of studies have been carried out in order to analyze the e
Publicado em: 2004