Adição de chamote de velas de ignição inservíveis na obtenção de cerâmica branca a base de alumina

AUTOR(ES)

Aldemiro José Rocha Palma

DATA DE PUBLICAÇÃO

2010

RESUMO

This work presents research into the addition of chamotte obtained from the ceramic isolator of unusable spark plugs in formulations of material mixes for standard white ceramic material with aluminum oxide bases. After the physical chemical characterization of the primary materials, standard clay and the chamotte, three mixtures were prepared with concentrations of 10, 20 and 30% chamotte by weight in relation to the standard clay. The test samples underwent heating at a rate of 30 0C/min to levels that included 100o , 200o , 300o, 400o, 500o e 600 0C and also we submitted to three distinct burn temperatures: 1450o, 1500o e 1550 0C, remaining at these temperatures for 2 hour periods. After sintering, the physical and microstructural properties of the different test samples were measured and analyzed. The results show that the materials obtained present good technical properties and that the chamotte can be reutilized as an additive in the production of white ceramic material with an aluminum oxide base

ASSUNTO(S)

engenharia mecanica cerâmica branca white ceramic material vela de ignição inservível reaproveitamento unusable spark plugs reutilization chamote

Documentos Relacionados

• Adesão a uma cerâmica aluminizada densamente sinterizada e a uma cerâmica a base de alumina
• Interfaces fracas em compósitos de matriz cerâmica de alumina/alumina
• Efeito da incorporação de chamote no processamento e microestrutura de cerâmica vermelha
• Desempenho do desgaste de cerâmica à base de alumina - uma revisão dos efeitos da microestrutura no desgaste erosivo
• Efeito da ignição por plasma na microestrutura e propriedades mecânicas do compósito alumina-níquel-cobalto