Assessment of concrete anisotropy by means of compression and indirect tensile tests
AUTOR(ES)
KOSTESKI, L. E.
FONTE
Rev. IBRACON Estrut. Mater.
DATA DE PUBLICAÇÃO
11/11/2019
RESUMO
Resumo Na análise e projeto estrutural de concreto armado, normalmente se assume que o material é isotrópico e homogêneo. As caraterísticas pontuais das estrutura, geralmente exercem pouca influência no comportamento das mesmas, portanto normalmente são desconsideradas. No entanto, existem muitas evidencias de que, na mesoescala, o concreto convencional apresenta algum grau de comportamento ortotrópico, que resulta do efeito gravitacional durante o lançamento o endurecimento do concreto. No presente trabalho são apresentados os resultados de ensaios de compressão axial e de tração por compressão diametral em corpos de prova cilíndricos. Os resultados destes ensaios confirmam que ambas, as resistências à compressão axial e à tração indireta, são perceptivelmente influenciadas pelo ângulo entre o eixo do corpo de prova e a direção de lançamento do concreto. Foi observado que a relação entre a resistência à compressão axial de um concreto de classe C50 obtida em cilindros moldados na posição horizontal e moldados na posição vertical é, em média, 0,85. Da mesma forma, a resistência à tração do concreto na direção vertical é, em média, cerca de 15% menor do que a resistência determinada empregando testes laboratoriais padrão.Abstract In reinforced concrete structural analysis and design it is normally assumed that the material is globally isotropic and homogeneous. Local departures from this model generally exert a minor influence on observed response and are therefore disregarded. There is overwhelming evidence, however, that in normal concrete there is some degree of meso-scale orthotropic behavior, which results from gravitational effects during concrete casting and hardening. In the present paper, results of compression tests, as well as indirect tensile tests using cylindrical samples, are reported. These tests confirm that both the unconfined compressive strength as well as the indirect tensile strength determined on cylindrical samples are perceptibly influenced by the angle between the sample axis and the vertical orientation during casting. It was determined that the ratio between the unconfined compressive strength of a C50 concrete mix measured in cylindrical samples cast in horizontal position and the strength of samples cast in horizontal position is on average 0.85. Similarly, the tensile strength of concrete in the vertical direction is, on average, also about 15% smaller than the strength determined employing standard laboratory tests.
Documentos Relacionados
- Appraising Vocational Fitness by Means of Vocational Tests
- Comparison of indirect hemagglutination and indirect immunofluorescence tests with microneutralization tests for detection of type-specific Herpesvirus hominis antibody.
- Serotypic classification of hantaviruses by indirect immunofluorescent antibody and plaque reduction neutralization tests.
- Compression tests of castor oil biopolymer
- Evaluation of plasticity and radiopacity of elastic separators by means of traction tests and radiography