Designing of CK45 carbon steel and AISI 304 stainless steel dissimilar welds
AUTOR(ES)
Pouraliakbar, Hesam, Hamedi, Mohsen, Kokabi, Amir Hossein, Nazari, Ali
FONTE
Mat. Res.
DATA DE PUBLICAÇÃO
11/10/2013
RESUMO
Gas tungsten arc welding of CK45 and AISI304 stainless steel was performed through preparation of different types of samples using ER308L and ERNi-1 wires. Welded samples were studied by different techniques including optical metallography, scanning electron microscopy equipped with energy dispersive X-ray spectroscopy (SEM-EDS), X-ray diffraction, hardness measurements and impact test. It was observed that in the buttered specimen, the structure of the weld metal was completely austenitic while the microstructure of unbuttered sample was duplex ferritic-austenitic. M23C6-type carbides were observed within the weld metal of both as-weld specimen types. Effects of different post-weld heat treatments (PWHTs) were investigated. The experimented results concluded that simultaneous grain growth and carbides precipitation were competitive during PWHT. Also, there were not any indication related to sigma-phase in as-welded and PWHTed specimens due to their lower Cr/Ni ratios and insufficient preservation times.
Documentos Relacionados
- Microstructural Transformations in Dissimilar Welds between Austenitic Stainless Steel and Ferritic Stainless Steel
- Nickel-Titanium Alloys Welding of Thin Sheets Using GTAW: Comparative Study Between Similar and Dissimilar Welding with AISI 304 Stainless Steel
- Investigação da tensão residual na soldagem laser entre o aço carbono AISI 1010 e o aço inoxidável AISI 304
- Effect of Continuous and Pulsed Current on the Metallurgical and Mechanical Properties of Gas Tungsten Arc Welded AISI 4340 Aeronautical and AISI 304 L Austenitic Stainless Steel Dissimilar Joints
- Nitriding of AISI 304 stainless steel by PIII in DC and RF toroidal discharges