Efeito da aplicação do gás ozônio na resistência de união entre resina composta e dentina / Effect of application of ozone gas in the bond strength between composite and dentin
AUTOR(ES)
Paula Cicília Faquim Rodrigues
DATA DE PUBLICAÇÃO
2009
RESUMO
The aim of this study was to evaluate the effect of ozone gas and its use with an antioxidant on the resin-dentin microtensile bond strength. The oclusal enamel of forty human third molars was then removed to expose a flat superficial dentin surface. The teeth were randomly divided into four groups (n = 10): (G1) untreated dentin with ozone (control group); (G2) ozone gas application for 40 s followed by acid etching; (G3) acid etching followed by ozone gas for 40s; and (G4) ozone gas for 40s with subsequent application of sodium ascorbato 10% for 10 min. Composite build-ups were constructed incrementally. Specimens were sectioned to obtain sticks with cross-sectional areas of 1mm2 to be tested in tension (0.5 mm/min). The microtensile bond strength values were analyzed by one-way ANOVA and Tukeys test (α=0.05). All sticks fractured were then observed under a stereomicroscope (40X). The results showed that the G1 had higher values of microtensile bond strength when compared to G2 and G3 (p=0.00). The values of microtensile bond strength of G1 and G4 were similar (p = 0158) and higher than the G2, but there was no difference between the values of G3 and G4 (p=0,115). The use of ozone prior to etching (G2) resulted in lower value of microtensile bond strength in all conditions evaluated (p = 0.00). The application of ozone gas decreased the microtensile bond strength of the interface dentin/composite resin, but the values were reversed when the use of sodium ascorbate
ASSUNTO(S)
materiais odontologicos ozone, antioxidants, composite resins, tensile strength ozônio, antioxidantes, resinas compostas, resistência à tração
Documentos Relacionados
- Efeito da aplicação do gás ozônio na resistência de união entre resina composta e dentina
- EFEITO DO NAOCL A 10% E DA APLICAÇÃO DO COMPÓSITO DE BAIXA VISCOSIDADE SOBRE A RESISTÊNCIA DA UNIÃO COMPÓSITO-DENTINA
- Efeito da ciclagem mecânica na resistência de união à dentina humana de uma resina composta associada a dois sistemas adesivos
- Durabilidade da união resina-dentina : efeito da umidade dentinaria na resistencia da união mediada por primers experimentais
- Effect of surface treatment and storage on bond strenght between indirect composite and self-adhesive cement