Effect of acid etching of glass ionomer cement surface on the microleakage of sandwich restorations
AUTOR(ES)
Bona, Álvaro Della, Pinzetta, Caroline, Rosa, Vinícius
FONTE
Journal of Applied Oral Science
DATA DE PUBLICAÇÃO
2007-06
RESUMO
The purposes of this study were to evaluate the sealing ability of different glass ionomer cements (GICs) used for sandwich restorations and to assess the effect of acid etching of GIC on microleakage at GIC-resin composite interface. Forty cavities were prepared on the proximal surfaces of 20 permanent human premolars (2 cavities per tooth), assigned to 4 groups (n=10) and restored as follows: Group CIE - conventional GIC (CI) was applied onto the axial and cervical cavity walls, allowed setting for 5 min and acid etched (E) along the cavity margins with 35% phosphoric acid for 15 s, washed for 30 s and water was blotted; the adhesive system was applied and light cured for 10 s, completing the restoration with composite resin light cured for 40 s; Group CIN - same as Group CIE, except for acid etching of the CI surface; Group RME - same as CIE, but using a resin modified GIC (RMGIC); Group RMN - same as Group RME, except for acid etching of the RMGIC surface. Specimens were soaked in 1% methylene blue dye solution at 24ºC for 24 h, rinsed under running water for 1 h, bisected longitudinally and dye penetration was measured following the ISO/TS 11405-2003 standard. Results were statistically analyzed by Kruskal-Wallis and chi-square tests (a=0.05). Dye penetration scores were as follow: CIE - 2.5; CIN - 2.5; RME - 0.9; and RMN - 0.6. The results suggest that phosphoric acid etching of GIC prior to the placement of composite resin does not improve the sealing ability of sandwich restorations. The RMGIC was more effective in preventing dye penetration at the GIC-resin composite-dentin interfaces than CI.
Documentos Relacionados
- Effect of antibacterial agents on the surface hardness of a conventional glass-ionomer cement
- Effect of etching and light-curing time on the shear bond strength of a resin-modified glass ionomer cement
- Microleakage on class V glass ionomer restorations after cavity preparation with aluminum oxide air abrasion
- Influence of acid etching on shear strength of different glass ionomer cements
- Comparasion of two minimally invasive methods on the longevity of glass ionomer cement restorations: short-term results of a pilot study