Energía calorífica necesaria, durante la soldadura en servicio de tuberías para el transporte de petróleo

AUTOR(ES)

Ramos Morales, Félix, Duffus Scott, Alejandro, Rodríguez Pérez, Manuel, Díaz Cedré, Eduardo M., Pozo Morejón, Juan A.

FONTE

Soldagem & Inspeção

DATA DE PUBLICAÇÃO

2009-03

RESUMO

The thermal behavior during in service repair welding of oil transportation pipes was studied by finite element analysis in the present paper. Regression equations that relate peak temperature at the inner surface of the pipe and cooling time between 800 and 500ºC in the heat affected zone to the welding heat input, preheat temperature, and convection heat transfer coefficient were obtained. The former parameters govern, respectively, the possibility of burn through and cold cracking, and the latter parameters define the thermal behavior during welding. The existence of conditions that simultaneously satisfy the obtained equations, for different combinations of related variables, was proved. Graphical representations of relevant practical importance that were developed from the solution of obtained equations are presented.

Documentos Relacionados

• Energía de ionización simple en la soldadura con electrodo revestido
• Comportamiento del tiempo de duración, la frecuencia de los cortocircuitos y la conductividad eléctrica durante el reencendido del arco en la soldadura SMAW (AC) con electrodos E6013
• Detección de perturbaciones en soldadura basado en el monitoreo de la acústica aerotransportada del proceso MIG
• Optimización de los Parámetros de Soldadura por Arco Sumergido en Acero HSLA: una Aplicación para Manufactura de Tuberías de Conducción de Hidrocarburos
• Derrota del conocimiento por la información: una reflexión necesaria para pensar en el desarrollo humano y la calidad de vida desde una perspectiva emancipadora