Estudo espectroscópico de vidros a base de aluminato de cálcio contendo Nd3+

AUTOR(ES)

Pecoraro, Édison, Nunes, Luiz Antonio de Oliveira, Sampaio, Jurací A., Gama, Sérgio, Baesso, Mauro L.

FONTE

Química Nova

DATA DE PUBLICAÇÃO

2000-04

RESUMO

Multicomponent ( Al2O3, CaO, SiO2, MgO) calcium aluminate-based glasses containing Nd3+ were prepared in order to evaluate their possibilities as laser host materials. The refractive index, UV-visible-near IR absorption spectrum, IR and visible luminescence spectra, and fluorescence decay time were measured. Judd-Ofelt model was used to obtain experimental intensity parameters ( omega2, omega4 and omega6), emission cross-section, radiative lifetimes, emission branching ratios and quantum efficiency.

Documentos Relacionados

• TransferÃncia E ConversÃo Ascendente de Energia em Vidros Tungstato-Fluorofosfatos Dopados com Tm3+ e Nd3+
• Investigação de vidros aluminato de calcio dopados com ions terras-raras
• Caracterização espectroscópica de possíveis meios ativos para lasers de Nd3+ e Tm3+
• Influencia dos metais de transição em vidros de aluminato de calcio e soda-lime
• Physical properties of low silica calcium aluminate glasses doped with NdO3 e Er2O3