Low Temperature Sintering of Aluminum-Zircon Metal Matrix Composite Prepared by Spark Plasma Sintering
AUTOR(ES)
Ghasali, Ehsan, Nouranian, Hossein, Rahbari, Ali, Majidian, Houdsa, Alizadeh, Masoud, Ebadzadeh, Touradj
FONTE
Mat. Res.
DATA DE PUBLICAÇÃO
12/09/2016
RESUMO
Aluminum-15 wt. % zircon metal matrix composite was fabricated using spark plasma sintering method at the temperature of 450°C and holding time of 4 min. The bending strength of 284±21 MPa and microhardness of 171±14 Vickers were determined for produced composite. XRD investigations proved that almost no decomposition of zircon particles as reinforcement occurred. SEM studies revealed the homogenous dispersion of reinforcement particles in the aluminum matrix.
Documentos Relacionados
- Spark Plasma Sintering of a Hard Metal Powder Obtained from Hard Metal Scrap
- WC-Co Particles Reinforced Aluminum Matrix by Conventional and Microwave Sintering
- Investigações sobre a sinterização de sílica vítrea por plasma pulsado.
- Analysis of the densification of a composite obtained by sintering process of aluminum bronze powders with different carbides
- Nanocompósitos de Al2O3-SiC sinterizados por "spark plasma sintering" (SPS)