Microstructural and Fractographic Characterization of a Thermally Embrittled Nuclear Grade Steel: Part I - Annealing
AUTOR(ES)
Tarpani, José R., Braz, Maria H.P., Bose Filho, Waldek W., Spinelli, Dirceu
FONTE
Materials Research
DATA DE PUBLICAÇÃO
2002-09
RESUMO
A nuclear reactor pressure vessel steel was submitted to different annealing heat treatments aimed at simulating neutron irradiation damage. The obtained microstructures were mechanically tested with subsequent metallographic and fractographic characterization. The relevant microstructural and fractographic aspects were employed in the interpretation of the mechanical behavior of the microstructures in both quasi-static (J-R curve) and dynamic (Charpy impact) loading regimes. A well defined relationship was determined between the elastic-plastic fracture toughness parameter J-integral and the Charpy impact energy for very most of the microstructures.
Documentos Relacionados
- Microstructural and Fractographic Characterization of a Thermally Embrittled Nuclear Grade Steel: Part II - Quenching and Tempering
- Sigma Phase in Superduplex Stainless Steel: Formation, Kinetics and Microstructural Path
- Characterization of Phase Transformations and Microstructural Changes in an API 5CT L80 Steel Grade During Ni Alloy Laser Cladding
- Microstructural characterization and mechanical behavior of a low-carbon 17%Mn steel
- Fractographic analysis of tensile failures of aerospace grade composites