Modeling of work hardening behaviour of high Mn and low C polycristalline austenitic steel with twip effect

AUTOR(ES)

Spindola, M.O., Ribeiro, E.A.S., Gonzalez, B.M., Santos, D.B.

FONTE

Matéria (Rio de Janeiro)

DATA DE PUBLICAÇÃO

2010

RESUMO

The steel of this work, 0.06C-25Mn-3Al-2Si-1Ni steel, presenting TWIP effect, was hot and cold rolled and then annealed at temperatures between 600 and 850ºC. The microstructure examination was focused in the recrystallization during annealing for different temperatures through optical and scanning electron microscopy. The volume fraction and recrystallized grain size measurements were performed. Tensile tests were conducted at room temperature. A polycrystalline model, based on micromechanics and working hardening theory, developed by Bouaziz et al., to predict the behavior of TWIP steels under different loading paths, was applied to the current steel. The results from the model are in good agreement with mechanical test and show a total elongation above 60%, uniform elongation up to 55% and a tensile strength greater than 600 MPa, which highlights the potential of this steel for its various applications, mainly automotive industry. The model parameters are discussed and their limitations are presented.

Documentos Relacionados

• Effect of Cold Work on Cavitation Resistance of an Austenitic Stainless Steel Coating
• Workhardening behaviour and microstructural analysis of failed austenitic manganese steel crusher jaws
• Effect of alloy grain size on the high-temperature oxidation behavior of the austenitic steel TP 347
• Low-temperature plasma nitriding of sintered PIM 316L austenitic stainless steel
• Study on microstructures and work hardening behavior of ferrite-martensite dual-phase steels with high-content martensite