Obtenção de filmes finos isolantes de SiO2 e Si3N4 por deposição quimica a fase vapor auxiliada por plasma remoto
AUTOR(ES)
William Cesar Mariano
DATA DE PUBLICAÇÃO
1996
RESUMO
Dieletric films, are used in a large amount of applications in semicondutors devices. Several plasma enhanced deposition techniques have been studied in order to obtain insulating materiais with quality that can be employed in processes of manufacturing of devices. In this work, depositions of two different dieletric films are studied, with two different techniques. Silicon oxide films were deposited by combination of two reactant gases: Silane (SiH4) and Oxygen (02) or Nitrous Oxide (N2O), in a temperature range from 300 to 600°C and in a Remote Enhanced Plasma Chemical Vapor Deposition - RPECVD system. Silicon Nitride films were obtained by Silane and Nitrogen (N2), in temperature range from 40 to 90°C and in a Electron Cyclotron Resonance Remote Plasma Enhanced Chemical Vapor Deposition, ECR - RPECVD system. The characterization of the films were: Deposition rate, Etching rate, Refractive index and Stoichiometry. Finally, the behavior of this characteristics versus process parameters were studied. The best processing conditions were determined Silicon oxide films with the following characteristics can be obtained: Deposition rate =100 Ã/min, Etch - rate = 170 Ãlmin, Refraction index = 1,465, Tensile stress = 1,2 X 1010 dyne/cm2 and Stoichiometry = 1,82. In the case of Silicon nitride, the best characteristics were: Deposition rate = 109 Ã/min, Etch rate = 190 Ã/min, Refraction index = 1,995 and Si/N = 0,75
ASSUNTO(S)
filmes finos nitreto de silicio oxidos plasma (gases ionizados)
ACESSO AO ARTIGO
http://libdigi.unicamp.br/document/?code=vtls000111823Documentos Relacionados
- Síntese e caracterização de nanocompósitos Ni: SiO2 processados na forma de filmes finos
- Filmes finos de SiO2 nanoporosos produzidos por irradiação iônica : dependência com a energia de irradiação e propriedades refletoras
- Avaliação das propriedades físico-químicas, mecânicas e tribológicas de filmes finos de VC, Si3N4 e TiN/Ti
- Catalisadores de Ni suportado em La2O3 e SiO2 aplicados na reação de reforma a vapor de glicerol
- Si3N4 ceramics sintered with Y2O3/SiO2 and R2O3(ss)/SiO2: a comparative study of the processing and properties