Structural and dielectric properties of ZrO2 added (Na1/2Bi1/2)TiO3 ceramic
AUTOR(ES)
Kumari, K., Prasad, K., Yadav, K.L., Sen, S.
FONTE
Brazilian Journal of Physics
DATA DE PUBLICAÇÃO
2009-06
RESUMO
Polycrystalline samples of ZrO2 added (Na1/2Bi1/2)TiO3 were prepared using high-temperature solid-state reaction method at 1050ºC and subsequent sintering at 1090ºC in air atmosphere. Rietveld analyses of XRD data indicated the formation of a single-phase hexagonal structure with R3c symmetry. Dielectric studies revealed the relaxor behaviour. The addition of ZrO2 to (Na1/2Bi1/2)TiO3 shifted phase transition temperature as well as depolarization temperature to higher side which is desirable for piezoelectric applications. The frequency dependence of the temperature of the permittivity maximum was modeled using Vogel-Fulcher relation. The dielectric relaxation in the system is found to be analogous to the magnetic relaxation in spin-glass system.
Documentos Relacionados
- ESTUDO DE FASES E CRESCIMENTO DE MONOCRISTAIS NO SISTEMA Bi2O3 - TiO2 - ZrO2
- Crystal growth; Photorefractive crystals; solid state synthesis; Bi2O3 - TiO2 - ZrO2
- Dielectric and Raman spectroscopy studies of (Na0.5Bi0.5)TiO3 lead-free ceramic
- Using ZrO2 or Al2O3 particles to enhance the mechanical properties of a LZSA glass-ceramic matrix
- Processamento e caracterização de cerâmicas de Ba2Ti9O20 sem e com Dopagens de ZrO2 para aplicação como ressoadores dielétricos de microondas