1. Biphasic 0.8BaTiO3/0.2Ni(1-x)CoxFe2O4 nanopowders by in situ sol-gel synthesis
Abstract Nanopowders of the 0.8BaTiO3/0.2Ni(1-x)CoxFe2O4 (x=0, 0.25, 0.5, 0.75, and 1) were synthesized by the in situ sol-gel method using poly(acrylic acid) (PAA1800) as a chelating agent. The synthesis developed using PAA1800 ensured the simultaneous crystallization of two phases. The results provided a reliable method for producing biphasic nanopowders i
Cerâmica. Publicado em: 2022
-
2. Phase transformation of kaolinite to hexagonal kalsilite using K2CO3
Abstract Hydrothermal synthesis of kalsilite was facilitated by the inclusion of potassium carbonate (K2CO3) as the source of the potassium ion. After a 24 h reaction at 220 °C, kaolin clay treated with 1.25 M K2CO3 showed the most significant peaks at 2θ of 28.5° and 34.7° by X-ray diffraction corresponding to the hexagonal kalsilite. In addition, field
Cerâmica. Publicado em: 2022
-
3. Production of nanostructured crystalline composite using residual ashes from flocculated sludge burning process in a poultry slaughterhouse wastewater treatment system
Abstract Nanostructured crystalline composite (activated carbon) was synthesized from residual ashes of the burning process of the sludge generated in the flotation step of a poultry slaughterhouse and was used for Allura red dye adsorption. The ashes were chemically activated using two types of reagents, H2O2 and H3PO4, and the structure, morphology, and su
Cerâmica. Publicado em: 2022
-
4. Microstructural characteristics, properties, synthesis and applications of mullite: a review
Abstract Mullite, an intermediate phase of the binary alumina-silica system, is one of the most important phases of ceramic products containing alumina and silica in the initial composition. Its stoichiometry ranges from 3Al2O3.2SiO2 (3:2) to 2Al2O3.SiO2 (2:1) and its crystalline structure is orthorhombic, characterized by the presence of octahedral chains o
Cerâmica. Publicado em: 2022
-
5. Dolomite-zirconia reaction sintered bonded coarse magnesia ceramics: effect of the bonding proportion
Abstract Refractory ceramic materials were manufactured, mainly composed of magnesia grains (coarse and medium fraction) and CaZrO3/MgO as a binding phase produced from the reaction sintering between CaMg(CO3)2 (dolomite) and m-ZrO2 (monoclinic zirconia), which constituted the finer fraction. Different relationships between the proportion and the size of the
Cerâmica. Publicado em: 2021-06
-
6. Editorial Comment: Luts-V: A new simplified score for assessing lower urinary tract symptoms in men
Abstract Refractory ceramic materials were manufactured, mainly composed of magnesia grains (coarse and medium fraction) and CaZrO3/MgO as a binding phase produced from the reaction sintering between CaMg(CO3)2 (dolomite) and m-ZrO2 (monoclinic zirconia), which constituted the finer fraction. Different relationships between the proportion and the size of the
Int. braz j urol.. Publicado em: 2021-06
-
7. Oxidative Stress & Male Infertility - A necessary and conflicted indissociable marriage: How and when to call for evaluation?
Abstract Refractory ceramic materials were manufactured, mainly composed of magnesia grains (coarse and medium fraction) and CaZrO3/MgO as a binding phase produced from the reaction sintering between CaMg(CO3)2 (dolomite) and m-ZrO2 (monoclinic zirconia), which constituted the finer fraction. Different relationships between the proportion and the size of the
Int. braz j urol.. Publicado em: 2021-06
-
8. Editorial Comment: Vasectomy re-reversal: effectiveness and parameters associated with its success
Abstract Refractory ceramic materials were manufactured, mainly composed of magnesia grains (coarse and medium fraction) and CaZrO3/MgO as a binding phase produced from the reaction sintering between CaMg(CO3)2 (dolomite) and m-ZrO2 (monoclinic zirconia), which constituted the finer fraction. Different relationships between the proportion and the size of the
Int. braz j urol.. Publicado em: 2021-06
-
9. Dysplasia of the fibrous sheath with axonemal and centriolar defects combined with lack of mitochondrial activity as associated factors of ICSI failure in primary ciliary dyskinesia syndrome
Abstract Refractory ceramic materials were manufactured, mainly composed of magnesia grains (coarse and medium fraction) and CaZrO3/MgO as a binding phase produced from the reaction sintering between CaMg(CO3)2 (dolomite) and m-ZrO2 (monoclinic zirconia), which constituted the finer fraction. Different relationships between the proportion and the size of the
Int. braz j urol.. Publicado em: 2021-06
-
10. Silicon carbide hollow fiber membranes developed for the textile industry wastewater treatment
Abstract In order to reduce the impacts of the industrial effluent on the environment, silicon carbide hollow fiber membranes were prepared by the precipitation-immersion technique and sintered at 1450 and 1500 °C. The membranes were characterized by X-ray diffraction, their surface structure was characterized by scanning electron microscopy and atomic forc
Cerâmica. Publicado em: 2021-06
-
11. QUANTIFICAÇÃO DE MULLITA PROVENIENTE DE RESÍDUOS DE CAULIM DA REGIÃO AMAZÔNICA: USO DO MÉTODO DE RIETVELD
Mullite is used to obtain a refractory material, there are several factors that influence the synthesis process of mullite: the preparation of the mixture, the precipitation and the reaction of SiO2 and Al2O3. For the synthesis of mullite, samples of kaolin processing residues were used as precursor material, because it presents SiO2 and Al2O3 in its composi
Quím. Nova. Publicado em: 2021-04
-
12. Cold sintering and electric characterization of ZnO-BaTiO3 composites
Abstract The sintering is an essential step in the processing of ceramics materials. A number of researchers have reported new techniques for sintering. However, in general, the process still demands high temperatures. This paper reports the results of the cold sintering of ZnO-BaTiO3 composites. The microstructural, structural, and electric properties of th
Cerâmica. Publicado em: 2021-03