Eutectic Carbides
Mostrando 1-9 de 9 artigos, teses e dissertações.
-
1. Mejora de la resistencia al desgaste abrasivo de un revestimiento Fe-Cr-Mn-C mediante la adición de V
ABSTRACT The aim of this work is to increase the abrasive wear resistance of a coating, applied on plates of AISI 1020 carbon steel, using tubular coated electrodes with the Fe-Cr-Mn-C alloy system. In order to achieve this increase, V was added to the alloy system. The resulting coating were studied using optical microscopy (MO), X-ray diffraction and micro
Matéria (Rio J.). Publicado em: 20/05/2019
-
2. Evolución microestructural durante el envejecimiento a alta temperatura de una aleación 35Ni-25Cr-Nb
ABSTRACT The dendritic-type microstructure of the 35Ni-25Cr-Nb alloy, in the as-cast condition, consists of an austenitic matrix and two types of eutectic primary carbides; Nb-rich MC type and Cr-rich M23C6 type both presents in interdendritic edges and grain boundaries. During aging at 800ºC for different times, M23C6 type secondary carbides precipitate in
Matéria (Rio J.). Publicado em: 19/07/2018
-
3. Influence of casting heterogeneities on microstructure and mechanical properties of austempered ductile iron (ADI)
ABSTRACT An investigation was carried out to examine the influence of as-cast heterogeneities on the resulting microstructure and mechanical properties of an austempered ductile cast iron (ADI). A commercial hypereutectic ductile iron alloy with 3.59% C, 2.68% Si, 0.24% Mn and 0.46% Cu (in wt. %) was produced in a coreless induction furnace. The specimens we
Matéria (Rio J.). Publicado em: 10/08/2017
-
4. Caracterização microestrutural da decomposição de carbonetos eutéticos M2C em ferro fundido multicomponente do tipo Fe-2C-5V-5Cr-5Mo-5W tratados isotermicamente à 950ºC e 1.050ºC. / Microstructural characterization of M2C eutectic carbides decomposition in multicomponent cast iron of type Fe-2C-5V-5Cr-5Mo-5W isothermically heat treated at 950°C e 1.050°C.
Multicomponent White Cast Iron are high temperature wear resistant ferrous alloys, presenting eutectic MC and M2C carbides in their as cast structure. In the present work the decomposition microstructures of the metastable M2C carbide after heat treatments was characterized in a model multicomponent white cast iron with composition (in weight): 2 wt% C and 5
Publicado em: 2010
-
5. Nucleation and growth of austenite/VC eutectic in alloys of the Fe-V-C system. / Nucleação e crescimento do eutético austenita/VC em ligas do sistema Fe-V-C.
The three most commercially important families of alloys for the foundry industry show the formation of faceted/non-faceted eutectics type during solidification: cast irons with graphite (austenite/graphite eutectic), white cast irons (austenite/carbide eutectic) and Al-Si alloys (alfa/silicon eutectic). In the case of white cast irons, the eutectic carbide
Publicado em: 2008
-
6. Influência de parâmetros microestruturais no comportamento tribológico de ligas ferrosas multicomponentes / Influence of microstructural parameters on the tribological behavior of multicomponent ferrous alloys
The aim of this work is to evaluate the effect of microstructural parameters (eutectic carbides and matrix hardness) of multi-component ferrous alloys on tribological behavior in sliding wear and micro-abrasive wear. The samples were two series of alloys with variable vanadium (V serie) and molybdenum (M serie) contents and fixed amounts of other elements. E
Publicado em: 2007
-
7. Desgaste e fadiga térmica de ligas aço matriz + NbC. / Wear and thermal fatigue of matrix steel + NbCalloys.
The concept of ?matrix steel + NbC? was used to cast alloys with the M2 steel matrix (0,5%C ? 2%W ? 3%Mo ? 4,6%Cr ? 1%V) and different volume fractions of niobium carbides. Niobium (2,5 e 5%) and stoichiometric carbon were added to produce NbC carbides and titanium (0,1%) to modify de NbC carbides morphology. NbC presented three basic morphologies: Chinese s
Publicado em: 2006
-
8. Fadiga térmica de ferros fundidos brancos multicomponentes. / Thermal fatigue of multicomponent white cast iron.
The effects of the volume fraction of eutectic carbides and of the matrix hardness on the thermal fatigue resistance of multicomponent white cast iron were investigated. Alloys Fe-4Cr-V-2Mo-2W-2C, V ranging from 5 to 8 wt% and Fe-4Cr-8V-Mo-2W-2C, Mo ranging from 2 to 5 wt % were used. Disc shaped samples were quench and tempered for obtaining two matrix micr
Publicado em: 2003
-
9. Fracture toughness of as-cast high speed steel M2, modified and heat treated. / Estudo da tenacidade à fratura do aço rápido M2 fundido, modificado e tratado termicamente.
Neste trabalho foi medida a tenacidade à fratura de quatro ligas fundidas com composição química base do aço AISI M2 uma de composição química convencional (liga I), e as demais modificadas por adições de nitrogênio (liga II), cério (liga III) e antimônio (liga IV) submetidas a tratamentos térmicos visando a decomposição do carboneto M2
Publicado em: 2001