1. Analysis of Residual Stress by the Hole-Drilling Method and Hardness in Dissimilar Joints of Austenitic Stainless Steel AISI 316L and Inconel 718 Alloy by Autogenous GTAW Process
Stainless steel and nickel alloy have high corrosion resistance in high-temperature environments due to the high Cr content present in their chemical composition, being widely used in components of nuclear reactors, petrochemical industries, etc. Through proper processes and procedures, it becomes possible to join these alloys. However, this union can genera
Mat. Res.. Publicado em: 02/12/2019
-
2. Interfacial bond-slip relationship between Carbon Fiber Reinforced Polymer Plate and Concrete after High Temperature of Asphalt Paving Construction
Abstract The bond-slip relationship of Carbon Fiber Reinforced Polymer (CFRP) plate-concrete after the influence of high temperature action of Stone Mastic Asphalt (SMA) paving was investigated in this article. Two groups of double shear specimens with different bonding length were designed and tested. Based on the test results, the failure modes of specimen
Lat. Am. j. solids struct.. Publicado em: 25/11/2019
-
3. The use of a liner under different bulk-fill resin composites: 3D GAP formation analysis by x-ray microcomputed tomography
Abstract Gap formation of composite resin restorations is a serious shortcoming in clinical practice. Polymerization shrinkage stress exceeds the tooth-restoration bond strength, and it causes bacterial infiltration within gaps between cavity walls and the restorative material. Thus, an intermediate liner application with a low elastic modulus has been advis
J. Appl. Oral Sci.. Publicado em: 25/11/2019
-
4. Resistência à Corrosão de Juntas Dissimilares dos Aços AISI 316L e da Liga Inconel 718
Resumo A soldagem dissimilar (Dissimilar Metal Welds – DMWs), união de dois diferentes materiais metálicos, tem muitas aplicações industriais, com destaque para trocadores de calor nas usinas nucleares. Portanto, devem resistir à corrosão e a esforços mecânicos, entre outros requisitos. Neste trabalho foi abordada a susceptibilidade à corrosão d
Soldag. insp.. Publicado em: 21/10/2019
-
5. Influence of coupling agents on the adhesion force of dissimilar overmolded polymers: a digital image correlation analysis
ABSTRACT The increase in the technical and functional requirements of plastic items has led the development of multimaterials. To achieve a good performance in the adhesion of dissimilar materials, in this case, polypropylene and coconut fiber composites, it is fundamental to understand the phenomena related to the specific interface. This work aims to evalu
Matéria (Rio J.). Publicado em: 16/09/2019
-
6. Effects of artepillin C on model membranes displaying liquid immiscibility
It has been hypothesized that the therapeutic effects of artepillin C, a natural compound derived from Brazilian green propolis, are likely related to its partition in the lipid bilayer component of biological membranes. To test this hypothesis, we investigated the effects of the major compound of green propolis, artepillin C, on model membranes (small and g
Braz J Med Biol Res. Publicado em: 25/03/2019
-
7. Shrinkage stress and elastic modulus assessment of bulk-fill composites
Abstract Bulk-fill composites were introduced in dentistry to accelerate clinical procedures while providing adequate outcomes. Concerns regarding the use of bigger composite increments rely on the polymerization shrinkage and shrinkage stress, which may generate gaps on the adhesive interface and result in a reduced success rate. Objective: To evaluate the
J. Appl. Oral Sci.. Publicado em: 07/01/2019
-
8. Effect of Solid Solution + Double Ageing on Microstructure and Properties in the Layer by Layer of the Z-Y Interface of Inconel 718 alloys Fabricated by SLM
The microstructure in the Z-Y surface of Inconel 718 alloys fabricated by selective laser melting (SLM) shows the relatively homogeneous and irregular fine grain structure after the heat treatment process of 1050ºC solid solution + double ageing. A large number of bulk precipitates were observed on the grain boundary, and the typical dendritic crystallizati
Mat. Res.. Publicado em: 11/10/2018
-
9. Minimization of polymerization shrinkage effects on composite resins by the control of irradiance during the photoactivation process
Abstract High levels of shrinkage stress caused by volumetric variations during the activation process are one of the main problems in the practical application of composite resins. Objective The aim of this study is to reduce the shrinkage stress and minimize the effects caused by composite resin volumetric variation due to the photopolymerization. In thi
J. Appl. Oral Sci.. Publicado em: 18/06/2018
-
10. Mechanical Loss Angle Measurement for Stressed thin Film Using Cantilever Ring-Down Method
Mechanical loss of the coating materials, and hence thermal noise from the mirror coatings, is a limiting factor for the sensitivity of the laser interferometer gravitational waves detector at its most sensitive frequency range. Mechanical loss of the thin films are often measured using the cantilever ring-down method. But when the thin film is under stress,
Mat. Res.. Publicado em: 28/05/2018
-
11. Effect of Loose Bonding and Corrugated Boundary Surface on Propagation of Rayleigh-Type Wave
Abstract The problems concerns to the propagation of surface wave propagation through various anisotropic mediums with initial stress and irregular boundaries are of great interest to seismologists, due to their applications towards the stability of the medium. The present paper deals with the propagation of Rayleigh-type wave in a corrugated fibre-reinforc
Lat. Am. j. solids struct.. Publicado em: 23/04/2018
-
12. Interfacial Shear Stress with Pull-out Test at Zeolite Ceramic Matrix and SS316 Single Fiber
ABSTRACT Natural zeolite ceramic is a material that can be used as bioceramics but it is fragile to crack. The weakness of ceramics can be overcome by making ceramic metals. The use of SS316 (stainless steel 316) fiber to strengthen the zeolite ceramic had been done in order to determine the interfacial relationship by using a fiber pull-out test. The conten
Matéria (Rio J.). Publicado em: 05/03/2018