1. Effect of Hot Deformation on Microstructure, Hardness and Precipitation Kinetics in a C350 Maraging Steel Modified by Titanium Addition
Maraging steels are alloys with a good balance between strength and fracture toughness. These properties are obtained by quenching and aging treatments, where the precipitation of intermetallic compounds is promoted in a martensitic matrix. In this context, this paper aims to evaluate the effect of hot deformation on microstructure, kinetics and formation of
Mat. Res.. Publicado em: 17/09/2018
-
2. Influence of Austenitizing on the Mechanical Properties of Maraging 300 and Sae 4340 Steels - Comparative Study
Maraging steels with 18wt%Ni and 10wt%Co are precipitation hardenable steels selected for special applications. These steels are quenched and aged in the 480 - 600ºC range. Ti and Mo are added to precipitate during aging as fine Ni3(Ti,Mo) and Fe2Mo particles. Aging at high temperatures causes overaging due to coarsening of particles and austenite formation
Mat. Res.. Publicado em: 02/05/2017
-
3. Short-term Creep Properties and Fracture Surface of 18 Ni (300) Maraging Steel Plasma Nitrided
Plasma nitriding of a solution annealed and aged 300 grade maraging steel was studied aiming to increase the creep resistance. The surface microhardness reached 1,140 HV, producing 50 µm layer composed of ε-Fe3N and γ'-Fe4N nitrides at the uppermost sample layer. The inner core remained unaltered presenting typical plate-like martensite microstructure of
Mat. Res.. Publicado em: 13/03/2017
-
4. Influence of Solution Annealing on Microstructure and Mechanical Properties of Maraging 300 Steel
Maraging 300 belongs to a family of metallic materials with extremely high mechanical strength and good toughness. Some works have been published about aging temperatures that improve ultimate strength resistance with acceptable toughness levels in this steel family, where the prior austenite grain size obtained by different solution annealing temperature in
Mat. Res.. Publicado em: 16/11/2016
-
5. Microstructural Analysis of Co-Free Maraging Steel Aged
ABSTRACT: Maraging steels have low carbon content and are highly alloyed, having as main feature the ability to increase the mechanical strength after thermal aging. Therefore, the objective of this work is to analyze the effect of aging in a Co-free maraging steel, Fe - 0.014% C - 0.3% Mn - 3.9% Mo - 2.1% Cu - 0.19% Si - 11.8% Cr - 9.1% Ni - 1.0% Ti (wt), a
J. Aerosp. Technol. Manag.. Publicado em: 2014-12
-
6. A dilatometric study of the phase transformations in 300 and 350 maraging steels during continuous heating rates
The influences of the chemical composition and heating rate have been studied in 300 and 350 maraging steels using dilatometry. For these tests, heating was carried out with heating rates of 1, 10 and 28 °C/s. The results have shown that the precipitation mechanism for both materials in the studied range is by lattice diffusion. Furthermore, Co and Ti conte
Mat. Res.. Publicado em: 10/05/2013
-
7. InfluÃncia do Resfriamento sub-zero apÃs o Envelhecimento na FormaÃÃo de Austenita Revertida em um AÃo Maraging 350 / Influence of sub-zero cooling after the formation of austenite on Aging Reversed in a maraging steel 350
Maraging steels are materials of ultra high strength mainly composed of a base quaternary Ni-Co-Mo-Ti which have excellent toughness combined with high mechanical strength being used in war industry, nuclear, aircraft components, pressure vessels up to the sports industry . One of its important applications is in use in hysteresis motors which require materi
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 29/09/2008
-
8. AnÃlise de Textura e Propriedades MagnÃticas em AÃos Maraging 300 e 350 em VÃrias CondiÃÃes de Tratamento / Analysis of Texture and Magnetic Properties of Maraging 300 and 350 in Various Conditions of Treatment
AÃos maraging sÃo ligas Ni-Co-Mo-Ti de ultra-alta resistÃncia e vasta aplicaÃÃo que vai desde a indÃstria bÃlica e nuclear atà componentes aeronÃuticos, vasos de pressÃo e a indÃstria esportiva. Atualmente estes aÃos vÃm sendo estudados para utilizaÃÃo em rotores de alta velocidade de motores de histerese. Os aÃos maraging apresentam algumas
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 25/08/2005
-
9. Efeito do tratamento termomecanico na microssegregação de um aço maraging grau 1900MPa
One of the main problems in the production of Maraging steels comes from banded structures. This banding is originated by interdendritic segregation during ingot solidification and persists in some degree after thermomechanicaltreatments. In this context, the present work studies the effect of thermomechanical treatments on the microsegregation of an electro
Publicado em: 1995