Spark Plasma Sintering
Mostrando 1-12 de 15 artigos, teses e dissertações.
-
1. Microstructure and diametral fracture strength of spark plasma sintered WC-6Co-0.2B and WC-6Co-0.5B ceramic composites from nanosized and metastable WC powders
Abstract The present work aimed at evaluating the microstructures and mechanical properties of spark plasma sintered WC-6 wt% Co ceramic composites doped with boron (0.2 and 0.5 wt%). W-50 at% C (W-6.13 wt% C) powders produced under different milling times (20, 60, 180, and 600 min) were used as starting materials and subsequently mixed with Co (6 wt%) and B
Cerâmica. Publicado em: 2022
-
2. Efeito da ignição por plasma na microestrutura e propriedades mecânicas do compósito alumina-níquel-cobalto
Resumo A técnica de spark plasma sintering (SPS) é um processo avançado de sinterização de materiais em baixas temperaturas e curto tempo por meio da formação de plasma em temperaturas muito altas em pequenos pontos e curtos tempos, pela qual os materiais de alta temperatura de sinterização podem sinterizar em temperaturas mais baixas. Neste estudo,
Cerâmica. Publicado em: 2018-09
-
3. Microstructural and Electrochemical behaviour of Aluminium Alloy Composites Produced Using Different Sintering Techniques
Present research work analyses the effect of heating modes on the densification, microstructure and mechanical properties of aluminum alloys [65Al-20Cu-15Mn] fabricated through powder metallurgy route. Sintering of compacts using conventional, microwave and spark plasma sintering methods has been carried out at 525°C. From the results, it has been observed
Mat. Res.. Publicado em: 12/03/2018
-
4. The Effect of Cr3C2 and TaC Additives on Microstructure, Hardness and Fracture Toughness of WC-6Co Tool Material Fabricated by Spark Plasma Sintering
Spark plasma sintering has been used to successfully produce WC-6Co-xCr3C2, WC-6Co-xTaC (x = 0.2, 0.6, 1.0) and WC-6Co-xCr3C2-xTaC (x = 0.1, 0.3, 0.5) cemented carbides. The spark plasma sintered compacts were investigated by scanning electron microscopy, hardness tests and fracture toughness tests. The results were compared to an additives-free WC-6Co cemen
Mat. Res.. Publicado em: 11/05/2017
-
5. Spark Plasma Sintering of a Hard Metal Powder Obtained from Hard Metal Scrap
Spark plasma sintering is used to consolidate a WC-Co powder produced from milled discharged hard metal cutting inserts. The powder was mixed to 10%wt Co powder and spark plasma sintered (SPS) under 80Mpa pressure, at 1200ºC with heating rate of 160ºC/min. A reference alloy was prepared with a commercial WC powder and 10%wt. Co under the same conditions. T
Mat. Res.. Publicado em: 13/03/2017
-
6. Avaliação da densificação do diboreto de titânio sinterizado por plasma pulsado
RESUMO O diboreto de titânio (TiB2) é um material cerâmico que se destaca por sua elevada resistência mecânica, estabilidade química e dureza a altas temperaturas, entretanto, características como baixa sinterabilidade e tenacidade a fratura limitam a atuação deste material em aplicações termomecânicas. Técnicas de sinterização não convencion
Matéria (Rio J.). Publicado em: 2016-12
-
7. Low Temperature Sintering of Aluminum-Zircon Metal Matrix Composite Prepared by Spark Plasma Sintering
Aluminum-15 wt. % zircon metal matrix composite was fabricated using spark plasma sintering method at the temperature of 450°C and holding time of 4 min. The bending strength of 284±21 MPa and microhardness of 171±14 Vickers were determined for produced composite. XRD investigations proved that almost no decomposition of zircon particles as reinforcement
Mat. Res.. Publicado em: 12/09/2016
-
8. Microstructures and Tensile Mechanical Properties of Consolidated Copper
Two consolidated copper samples were prepared by consolidation of a gas atomized powder using two different routes of spark plasma sintering (SPS), respectively. The first route was direct SPS of copper powder at 800 °C for 10 minutes, and the second route was compacting copper powder by die-pressing to produce a powder compact followed by SPS of the powder
Mat. Res.. Publicado em: 04/12/2015
-
9. Investigações sobre a sinterização de sílica vítrea por plasma pulsado. / Investigations of vitreous silica sintering by spark plasma.
A obtenção da sílica vítrea pelo processo de sinterização por plasma pulsado (SPS), a partir de matérias-primas de diferentes estruturas (cristalina e amorfa) e diferentes granulometrias, foi investigada. Análises de difração de raios X, transmitância óptica, microscopia óptica e eletrônica de varredura, e medições de densidade foram realizad
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 30/06/2011
-
10. Study of electrical properties of 2- and 3- dimensional carbon nanotubes networks
Redes bi- e tridimensionais de nanotubos de carbono (2D e 3D-RNTCs) foram preparadas sobre substratos de vidro de sílica e em matriz de sílica, respectivamente. Vários tipos de nanotubos de carbono (nanotubos de carbono de paredes simples, dupla e multicamadas, NTCPSs, NTPDs e NTPMs respectivamente) foram caracterizados por microscopia eletrônica de tran
Publicado em: 2011
-
11. Synthesis and characterization of PB IND.1-XR IND.XZR IND.0,40TI IND.0,60O IND.3(R = La, Ba) / Síntese e caracterização estrutural e dielétrica de compostos ferroelétricos PB IND.1-XR IND.XZR IND.0,40TI IND.0,60O IND.3(R = La, Ba)
O titanato e zirconato de chumbo PB(ZR1-yTIy)O IND.3é um material ferroelétrico de estrutura perovskita que tem sido aplicado como transdutores, amplificadores, sensores piezoelétricos, piroelétricos e memórias ferroelétricas. É bem estabelecido que a incorporação de íons de LA POT.3+ou BA POT.2+nos sítios ocupados pelo PBno sistema PB(ZR1-yTIy)O(
Publicado em: 2011
-
12. Otimização topológica de transdutores piezelétricos com gadação funcional de material: projeto, simulação, análise e fabricação. / Topology optimization of piezoelectric transducers considering functionally graded material: design, simulation, analysis and fabrication.
Piezoelectric materials generate displacements when they are excited by electrical potential and electrical potential when they are excited by force or pressure. These materials are widely applied in Precision Mechanics, Mechatronics, and Ultrasonic imaging areas. On the other hand, Functionally Graded Materials (FGM) are advanced materials, whose properties
Publicado em: 2010